摘 要

由于压敏胶的广泛应用，其性能的要求也随之提高。不同类产品的压敏胶要求也有所不同，本文主要讨论的丙烯酸酯压敏胶，其中兼具乳液型和溶剂型的水性丙烯酸压敏胶因具备优良的性能和无污染等特点成为了此次实验研究的重点。此次实验的目的是通过实验的方法来解决原样压敏胶初粘性低的问题。

本文是以丙烯酸丁酯和丙烯酸异辛脂作为聚合软单体，丙烯酸为硬单体，丙烯酸羟丙酯为功能单体，添加反应型乳化剂等来改善性能。软硬单体的配比决定了产物的玻璃化温度，从而决定了产品的初粘性。所以本实验通过控制软硬单体的配比和软单体各组分的配比来进行实验,当软硬比例为9:1;同时丙烯酸丁酯与异辛脂的比例为1:1.39时所得产物性能最好。

关键词: 压敏胶 丙烯酸酯 玻璃化温度 初粘性 软硬单体

Abstraction

Due to the wide application of pressure sensitive adhesive, the requirements of its performance are also improved. Different kinds of products of pressure-sensitive adhesive requirements are different, mainly discussed in this paper is acrylic pressure-sensitive adhesive, which both emulsion type and solvent type water-borne acrylic pressure sensitive adhesive due to have excellent performance and no pollution characteristics become the focus of the experimental study. The purpose of this experiment is to solve the problem of initial low viscosity of the original pressure sensitive adhesive by experiments.

This experiment is to butyl acrylate and acrylic acid ISO octyl ester as polymerization soft monomer, acrylic acid as hard monomer, 2 – ethylhexyl acrylate as the functional monomer, add reactive emulsifier etc. to improve performance. The ratio of the hard and hard monomers determines the glass temperature of the product, which determines the initial viscosity of the product .So the experiment was carried out by controlling the ratio of the soft monomer and the composition of the soft monomer, When the soft and hard ratio of 9:1, at the same time, the ratio of butyl acrylate and the proportion of butyl ester was 1:1.39, the product performance is best.

Keywords: pressure sensitive adhesive, acrylate, glass state temperature ; initial viscosity, soft and hard monomer

目录

摘要 II

Abstraction II

1 前言 1

1.1 压敏胶概述 1

1.1.1压敏胶的定义 1

1.1.2压敏胶的分类 1

1.1.2压敏胶的应用 2

1.2丙烯酸压敏胶的概况 2

1.2.1丙烯酸压敏胶的特点 2

1.2.1丙烯酸压敏胶的构成 3

1.2.3丙烯酸压敏胶的分类 3

1.3水性丙烯酸压敏胶的概况 4

1.3.1水性丙烯酸压敏胶的现状及发展 4

1.3.2水溶性丙烯酸压敏胶的特点 5

1.3.3水性丙烯酸压敏胶的改性 5

2实验部分 7

2.1实验药品 7

2．2验设备及仪器 7

2.3 实验方法 7

2.4 具体步骤 9

3.测试仪器及测试 10

3.1树脂外观测试 10

3.2固含量的测定 10

3.3 产物粒径的测试 10

3.4 粘度的测试 11

4 结果与讨论 11

4.1水性丙烯酸压敏胶的性能影响因素 11

4.2 软单体组成对压敏胶性能的影响 11

4.3 压敏胶粒径对其性能的影响 12

4.4 固含量对压敏胶性能的影响 12

4.5 数据分析 12

5 结论 13

参考文献 14

致谢 16

高性能水性丙烯酸酯压敏胶的制备与表征

1 前言　　

压敏胶(PSA) 是一类无需借助于溶剂或热，只需施加轻度压力，就能与物体牢固粘接的胶粘剂。由于它具有持粘力大、初粘力高，如不被污染则能够反复使用，且揭开后一般不影响被粘物表面等优点，因此在汽车装饰、医疗卫生、军用制品、彩色扩印、电工绝缘等多种领域中得到了广泛的应用。

1.1 压敏胶概述

1.1.1压敏胶的定义

压敏胶是压敏胶粘剂的简称。是一类具有对压力有敏感性的胶粘剂。主要用于制备压敏胶带。一般压敏胶的剥离力（胶粘带与被粘表面加压粘贴后所表现的剥离力）lt;胶粘剂的内聚力（压敏胶分子之间的作用力）lt;胶粘剂的粘基力（胶粘剂与基材之间的附着力）。这样的压敏胶粘剂在使用过程中才不会有脱胶等现象的发生。

1.1.2压敏胶的分类

压敏胶按其主体可以分为树脂型和橡胶型两大类，具体又可分为橡胶型压敏胶、热塑性弹形体压敏胶、有机硅类压敏胶，聚氨酯压敏胶和丙烯酸酯压敏胶五大类。

（1） 橡胶型压敏胶