#160;tio2 是新一代催化剂载体材料，能够与催化剂的活性组分发生”强相互作用”，可显著提高催化剂的单位活性，在加氢脱硫、选择性催化还原和低温氧化等与环境相关的催化反应中表现出了良好的应用潜力。
然而，目前鲜见 tio2 作为催化剂载体大规模工业应用的相关报道。
常规的 tio2 存在比表面积低（ 2/g）、热稳定性差（在 550 oc 时发生锐钛矿转成金红石相）、机械性能低（抗破碎强度 1~2 n/mm）等结构问题，普遍观点认为比表面积低导致 tio2 负载的活性组分量少，进而降低了反应活性位的数量，最终造成 tio2 催化剂整体的催化性能不佳。
剩余内容已隐藏，您需要先支付后才能查看该篇文章全部内容！
2. 参考文献
#160;
1.Sijia Liu, et al. Temperature sensitive synthesis of γ-Al2O3 support with different morphologies for #160;#160;#160;#160;#160;#160;CoMo/γ- Al2O3 catalysts for hydrodesulfurization of thiophene and 4,6-dimethyldibenzothiophene. Catalysis Science Technology . 2017, 7:466#8211;480
2.P. Afanasiev.Calculation of MoS2 slabs morphology descriptors from transmission electron microscopy data revisited Case study of the influence of citric acid and treatment conditions on the properties of MoS2/Al2O3. Applied Catalysis A: General.2017,529:10-19
3. Huan Liu, et al.One-pot synthesis of ordered mesoporous NiMo-Al2O3 catalysts for dibenzothiophene hydrodesulfurization. Applied Catalysis B: Environmental .198 (2016) 493#8211;507
4.O.V. Klimov, et al.CoNiMo/Al2O3 catalysts for deep hydrotreatment of vacuum gasoil. catalysis today.271 (2016) 56-63
5.Yasuaki Okamoto, et al.Effect of sulfidation atmosphere on the hydrodesulfurization activityof SiO2-supported Co#8211;Mo sulfide catalysts: Local structure andintrinsic activity of the active sites. Journal of Catalysis .268 (2009) 49#8211;59
6.Yasuaki Okamoto, et al.Effect of sulfidation atmosphere on the hydrodesulfurization activity of SiO2-supported Co#8211;Mo sulfide catalysts: Local structure and intrinsic activity of the active sites. Journal of Catalysis . 268 (2009) 49#8211;59
7.P Castillo-Villal#243;n, et al. Influence of the support on the catalytic performance of Mo, CoMo, and NiMo catalysts supported on Al2O3#160;and TiO2#160;during the HDS of thiophene, dibenzothiophene, or 4,6-dimethyldibenzothiophene. Catalysis Today. 2016 (112) 245-257
8.Y Zhuhong, et al. Preparation of Nickel Phosphide/Mesoporous-TiO2#160;Catalyst and Its Hydrode-
#160;#160;#160;#160;#160;#160;#160; -sulfurization Performance. Chinese Journal of Catalysis. 2012(33) 508-517
9.Licheng Li, et al.Carbon heterogeneous surface modification on a mesoporous TiO2-supported #160;#160;#160;#160;#160;catalyst and its enhanced hydrodesulfurization performance. ChemComm. 2012, 48, 11525#8211;11527
3. 毕业设计（论文）进程安排
第一阶段：翻译外文文献；
#160;#160;#160;#160;#160; ↓
第二阶段：根据课题要求，查阅文献；
#160;#160;#160;#160;#160; ↓
第三阶段：撰写开题报告；
#160;#160;#160;#160;#160; ↓
第四阶段：开展相关实验；
#160;#160;#160;#160;#160; ↓
第五阶段：数据处理，撰写论文；
#160;#160;#160;#160;#160; ↓
第六阶段：论文预答辩和终答辩。
剩余内容已隐藏，您需要先支付 10元 才能查看该篇文章全部内容！立即支付